Self-organized templates provide backbone for all integrated Li-ion batteries
Kiyoung Lee, Patrik Schmuki
2015
NPG Asia Materials
Batteries as well as modern supercapacitors involve a surface redox reaction and an ion intercalation process on anodes and cathodes. For an optimum electrode performance, a broad range of ion intercalation materials in nanoscale morphologies is currently being investigated. The nanoscale assembly of electrodes is not only crucial to maximize the specific surface area (volumetric charging capacity with ions or electrons) and to efficiently use an optimized ion interaction thickness (solid state
more »
... diffusion of the intercalating species of a few nm). However, classic geometries involving two nanostructured electrodes (such as in Figure 1a ) arranged either in a parallel or interdigitated configuration have limitations in view of an efficient intercalation reaction, especially at high charging/discharging rate due to (diffusion limited) Li ion depletion within the nanostructures or an irregular charge distribution along the nanostructure scaffold. [1] [2] [3] The recent work by Rubloff et al. 4 suggests another highly original, yet strikingly simple concept to tackle these issues. The authors directly fabricate a full-cell Li-ion battery by depositing anode and cathode into pores of self-organized alumina oxide (Figure 1b) based on a set of entirely self-ordering construction steps. As substrate for the battery serves a selforganized porous alumina template that inherently provides a number of geometrical optimization features (length and diameter of pores)-but moreover the partial filling of the tubes with the Ru/V 2 O 5 electrode materials seems to be adjustable simply by the penetration depth of the atomic layer deposition (ALD) process of the respective materials. In the present concept, a conformal ALD wall cladding of Ru/crystalline α-V 2 O 5 is used as an anode and Ru/prelithiated V 2 O 5 (Li x V 2 O 5 ) is used as a cathode (Ru metal is considered to act as a current collector). Except for the simplicity of the concept, the most beneficial effect of the configuration is the fully contacted electrolyte on each electrode, a short Li ion diffusion length and a high ionic conductivity that combined lead to a high specific capacity. 5 From a fundamental scientific viewpoint, it is worth noting that the work reaches extremely interesting electrochemical dimensions where classic intercalation (battery) and classic surface charging (supercapacitors) begin to unify. At present, the absolute performance of this new one-dimensional design has not yet reached the level of commercial battery devices; nevertheless, there is sufficient room for optimization to make this concept a cornerstone for future generation of thin-film energy storage devices.
doi:10.1038/am.2015.44
fatcat:kshrmce2fnbtxnb3wok7qwuz7a