Effect of intrinsic pigmentation on the flexural strength of a microwave-cured acrylic resin

Frederico Augusto Peixoto Silva, Tatiana Bernardon Peixoto Silva, Altair Antoninha Del Bel Cury
2002 Brazilian Dental Journal  
This study investigated the effect of intrinsic pigmentation on the transverse strength of a microwave-cured acrylic resin. Forty transverse strength specimens were fabricated according to ADA specification #12 and divided into 5 groups. No fibers were added to group I (GI, control group); acrylic stain (AS) was added to GII and GIII in concentrations of 0.5 and 1.5% w/w, respectively; acrylic fibers (AF) were added to groups GIV and GV in concentrations of 0.5 and 1.5% w/w, respectively. All
more » ... respectively. All specimens were irradiated in a microwave oven with a cycle of 3 min at 360 W, followed by 4 min resting, then 3 min at 810 W. Flasks were bench-cooled for 30 min at room temperature, followed by immersion in cold tap water for 30 min. After storage in distilled water at 37ºC for 48 h, all specimens were tested for flexural strength in a testing machine (EMIC-DL 500) at a crosshead speed of 0.5 cm/min. Mean and standard deviation (MPa) for the flexural strength test were: GI=86.0 ± 7.9; GII=86.0 ± 9.8; GIII=86.6 ± 7.7; GIV=84.9 ± 5.3; GV=84.9 ± 5.2. No statistical differences were detected among the groups (ANOVA, p>0.05). The addition of the acrylic fibers or the acrylic stain did not affect the transverse strength of the microwave-cured acrylic resin.
doi:10.1590/s0103-64402002000300013 pmid:12428598 fatcat:zlkzn7mjcnhxvl2ddm2odqgh2a