Effect of Intercritical Deformation on Bainite Formation in Al-containing TRIP Steel

Haiwen Luo, Lie Zhao, Suzelotte O. Kruijver, Jilt Sietsma, Sybrand van der Zwaag
2003 ISIJ International  
The Influence of intercritical deformation, cooling rate and prior austenite grain size on bainite formation were investigated by dilatometry tests. Intercritical deformation (0-40 %) performed in steels with a prior austenite grain size of 15-28 mm leads to formation of more ferrite during the cooling and less bainite during the subsequent isothermal stage, and even almost no bainite is formed after 40 % strain. Fast cooling after deformation can suppress ferrite transformation. Relaxation
more » ... owing deformation can significantly, but not completely, reduce such effect of deformation due to the occurrence of recovery and recrystallization, particularly for the finer prior austenite grain size. When the prior austenite grain size was changed from 26.8 to 16.8 mm, bainite formation was suppressed. The mechanism for influence of deformation on bainite formation was discussed on the basis that deformation could refine the austenitic microstructure. Further, it is suggested that there is a critical size of austenite grains or subunits after deformation for the formation of bainite. Fig. 7. Austenite fraction transformed during the cooling from 740 to 400°C and the following isothermal stage at 400°C for bainitic treatment. (a) No relaxation after deformation and (b) relaxation for 60 s after deformation. Fig. 8. Intercritical deformation resulted in deformation bands (indicated by arrows) in austenite, which then transformed to ferrite and divided austenite grains into several parts. Specimens were deformed to (a) 0, (b) 20 %, (c) and (d) 40 % and then directly cooled to 400°C at 20°C/s for bainite formation. Fig. 9. Austenite fraction transformed during the cooling from 740 to 400°C at the cooling rate of 50°C/s and the following isothermal stage at 400°C for bainitic treatment.
doi:10.2355/isijinternational.43.1219 fatcat:zbmw4kf3mzci5mrhq3xcytynsu