Eu and Dy Co-activated SrB2Si2O8 Blue Emitting Phosphor: Synthesis and Luminescence Characteristics
English

T. Q. Leow, R. Hussin, Z. Ibrahim, K. Deraman, W. N. W. Shamsuri, H. O. Lintang
2015 Sains Malaysiana  
The main focus in this research was to understand the influence of Dy 3+ and Eu 3+ doping/co-doping and sintering atmosphere on the luminescence properties of SrB 2 Si 2 O 8 . Single phase Eu and Dy doped/co-doped SrB 2 Si 2 O 8 ceramics were synthesized in different atmosphere through solid state reaction technique. An inexpensive method was occupied to provide reducing sintering atmosphere. Europium doped SrB 2 Si 2 O 8 exhibit unusual reduction from trivalent to a divalent oxidation state
more » ... oxidation state even in an oxidizing atmosphere. We also discovered co-doping with Dy 3+ ions produced further europium reduction in this phosphor. By manipulating the sintering condition and co-doping, a reddish-purple to blue tune-able phosphor under 390 nm excitations were produced and their Commission International del'Eclairage (CIE) color coordination were calculated and plotted in a CIE ABSTRAK Fokus utama dalam kajian ini adalah untuk memahami pengaruh pengedopan Dy 3+ dan Eu 3+ dan juga atmosfera pensinteran pada ciri-ciri luminesen SrB 2 Si 2 O 8 . Fasa tunggal seramik SrB 2 Si 2 O 8 yang didopkan dengan Eu dan Dy telah disintesis dalam suasana yang berbeza melalui teknik tindak balas keadaan pepejal. Kaedah yang berkos rendah telah digunakan untuk menyediakan suasana pensinteran menurun. SrB 2 Si 2 O 8 yang didopkan dengan europium menunjukkan penurunan yang luar biasa daripada keadaan pengoksidaan trivalen kepada dwivalens walaupun dalam suasana pengoksidaan. Kami juga mendapati pengedopan bersama dengan ion Dy 3+ menghasilkan lebih penurunan europium dalam fosfor ini. Dengan memanipulasikan atmosfera pensinteran dan pengedopan, sinaran merah-ungu ke biru diperoleh apabila fosfor dipancar dengan ujaan sinaran 390 nm. Koordinasi warna Jawatan kuasa Antarabangsa del'Eclairage (CIE) fosfor tersebut telah diambil dan diplotkan dalam gambar rajah CIE 1931. Spektra fotoluminesen fosfor SrB 2 Si 2 O 8 yang didopkan bersama dengan Eu 2+ /Eu 3+ dan Dy 3+ menunjukan pemindahan tenaga daripada Dy 3+ ke Eu 3+ dan Eu 2+ yang boleh diperhatikan dalam transisi pengujaan f-f dari Dy 3+ dan Dy-O band pemindahan caj. Sinaran 777 nm yang lemah daripada transisi ion O 2-3p 5 P ke 3s 5 S 0 juga diperhatikan dalam semua sampel. Puncak pengujaan dan pemancaran transisi f-f dari Dy 3+ dan Eu 3+ disertakan dengan transisi 4f -5d dari ion Eu 2+ juga dibincangkan. Jalur pengujaan yang panjang dalam rantau ultraungu (UV) daripada seramik SrB2Si2O8 didopkan dengan logam nadir bumi menghasilkan fosfor yang boleh diuja dalam UV dengan berkesan demi kegunaan dalam pencahayaan keadaan pepejal. Kata kunci: Eu 3+ pengurangan udara; fotoluminesen; pemindahan tenaga; pengedopan; SrB 2 Si 2 O 8
doi:10.17576/jsm-2015-4405-16 fatcat:zoy4cl7unfa43bbkanxmg2ylmm