The Microstructure and Wear Resistance of the Ti-assisted Hot Plasma Nitrided Layer
2019
Medžiagotyra
In order to improve the wear resistance of the surface nitrided layer of 1060 aluminum matrix, the nitrogen containing thermal plasma Ti-assisted nitriding method was adopted to obtain the strengthening phases of AlN and TiN simultaneously. The influence of the nitriding technological parameter on Ti-assisted nitriding was studied through changing the nitrogen containing thermal plasma current (I = 100 to 160 A) and the flow ratio of the nitriding atmosphere (Ar/N2 = 8/2, 6/4, 4/6 and 2/8