Study Of Pb(Zr0.65Ti0.35)O3(PZT(65/35) Doping On Structural, Dielectric And Conductivity Properties Of BaTiO3(BT) Ceramics

Arun Chamola, Hemant Singh, U. C. Naithani
2011 Advanced Materials Letters  
1−x)BaTiO 3 -xPZT(65/35) ceramics were prepared by high temperature solid state reaction technique. Structural properties of the compounds were examined using an X-ray diffraction (XRD) technique to confirm the formation of phase at room temperature. Detailed studies of dielectric properties of (1−x) BaTiO 3 -xPZT(65/35) for all compositions were in temperature range 30-200 o C reveal that the compound have transition temperature well above at the room temperature. While pure BaTiO 3 ceramics
more » ... hibited a sharp phase transformation expected for normal ferroelectrics, phase transformation behavior of the (1−x) BaTiO 3 -xPZT(65/35) solid solutions became more diffuse with increasing PZT(65/35) contents. The diffusivity of the dielectric peaks in the compound exhibited the values between 1 and 2 where the higher value indicates the greater disorder in the systems. This was primarily evidenced by an increased broadness in the dielectric peak, with a maximum peak width occurring at x = 0.5. The temperature dependence of ac conductivity indicated that the electrical conductivity decrease above T C on increasing the PZT(65/35) contents. This increase in the conductivity is attributed to the increase in polarizability of the materials around T c, due to oxygen vacancies.
doi:10.5185/amlett.2010.11183 fatcat:xg7halq265gbhb2hxga3ie42lq