Microstructural and mechanical properties of Ni-YSZ fabricated using SPS processing have been investigated at various sintering temperatures. Our study shows samples to be applied as a SOFC anode have the proper porosity of 40% and high hardness when processed at 1100ºC. These results are comparable to the values obtained at 100-200ºC higher sintering temperature reported by others. This result is important because when the fabrication processes are performed above 1100ºC, the mechanical

more »

... y starts to decrease drastically. This is caused by the fast grain coarsening at the higher temperature, which initiates a mismatch between thermal expansion coefficients of Ni and YSZ and induces cracks as well.