The goal of this investigation was to produce a zirconia-family black ceramics that has enhanced functionality and reliability. Color zirconia ceramics have been produced by adding pigments. Pigments cause structural defects within zirconia and result in a drop in physical properties. Using environmentally friendly rice husk, we produced a black zirconia that is free of structural defects. In optimal firing conditions for black zirconia the calcining temperatures of the molding product are

more »

... ed from 400 o C to 1200 o C, and the firing temperatures are changed from 1400 o C to 1600 o C. Color of testing the specimens was analyzed using Ultraviolet (UV) spectroscopy. Scanning Electron Microscope (SEM), EDAX (EDX), and Fourier transform infrared spectroscopy (FT-IR) analyses were carried out in order to examine impregnation properties and crystal phases. Universial Test Machine (UTM) was used to measure the flexual strength as well as the compressive strength. From experimental results, it was found that in optimal firing conditions the sample was calcined from 1000 o C to 1500 o C. Commission internationalde I'Edairage (CIE) values of manufactured black zirconia color were L* = 29.73, a* = 0.23, b* = −2.68. The bending strength was 918 MPa and the compressive strength was 2676 MPa. These strength values are similar to typical strength values of zirconia, which confirms that carbon impregnation did not influence physical properties.