Tensile and compressive strength tests were conducted to investigate the mechanical characteristics of aluminized paraffin wax fuel for hybrid gas generator applications. Mixtures of 0 wt%, 10 wt% and 30 wt% nano aluminum paraffin coupons as well as 5 wt%, 10 wt% and 15 wt% micro aluminum paraffin coupons were used. The average particle size of 100nm and of 8m mixed each with microcrystalline paraffin wax(Sasol 0907) were chosen for the base specimens where the tensile strength test followed

more »

... e ASTM-D638 specimen standard while the compressive strength test followed the ASTM D575-91. It was found that nano based specimens increased both the tensile and compressive strength enhancing the mechanical behavior of paraffin wax whereas the micro based specimens gave still less influential effect. 초 록 본 연구에서는 하이브리드 가스 발생기용 파라핀/알루미늄 왁스 연료의 기계적 특성 파악을 위한 인 장 및 압축강도 실험을 수행하였다. 혼합된 알루미늄 입자의 크기와 첨가량에 따른 기계적 특성을 파 악하기 위해 10 wt%, 20 wt%, 30 wt%의 나노 입자 첨가 시편과 5 wt%, 10 wt%, 15 wt%의 마이크로 입자 첨가 시편을 사용하였다. 평균입도 100 nm 및 8 m 크기의 알루미늄 입자와 Sasol사의 미정질 파라핀 왁스(Sasol 0907)를 이용하였고, 인장시험과 압축 시험에 사용된 시편은 각각 ASTM-D638, ASTM D575-91 규격에 따라 제작하였다. 나노 입자의 첨가는 시편의 인장 및 압축강도를 크게 향상시 키나 마이크로 입자의 첨가는 상대적으로 인장 및 압축강도의 증가에 미치는 영향이 미미한 것으로 파 악되었다.