Characterization And Study Of Iron(III)-Released From Alginate/Zeolite/Fe Composite

Nia Silvia Sukma, Yateman Arryanto, Sutarno Sutarno
2016 Eksakta: Jurnal Ilmu-Ilmu MIPA  
Alginate is an organic polymer that is isolated from brown algae and bacteria, while the zeolite is an aluminosilicate mineral sample. The purpose of this study was to synthesize composite alginate / zeolite / Fe, characterize composite alginate / zeolite / Fe, and assessing the release properties of Fe (III) of the composite alginate / zeolite / Fe. Characterization of the composite is done by observing the color composite macroscopically, and observing the pattern of distribution of zeolite
more » ... rticles in composites using SEM (Scanning Electron Microscope). As for assessing the release of Fe (III) of the composite system made by soaking the composite in a solution of citric acid 0,33M for nine hours. Components of Fe (III) were dissolved in acid systems were analyzed using UV-Vis spectrophotometer. The results showed that the composite alginate / zeolite / Fe have colors that are significantly dependent on the component ratio of alginate and zeolitnya. SEM analysis provides information that the zeolites distributed evenly on alginate-Fe phase. The release profile of Fe (III) of the composite alginate / zeolite / Fe weight variation component alginate produced three mechanisms to increase and decrease the rate of release of Fe (III). While the release profile of Fe (III) of the composite alginate / zeolite / Fe by weight of the zeolite component generates two mechanisms that increase and decrease the rate of release of Fe (III). Keywords: alginate/zeolite/iron composite, characterization, study of iron release ABSTRAK Alginat adalah suatu polimer organik yang diisolasi dari ganggang coklat dan bakteri, sedangkan zeolit merupakan contoh mineral aluminosilikat. Tujuan dari penelitian ini adalah untuk mensintesis komposit alginat/zeolit/Fe, mengkarakterisasi komposit alginat/zeolit/Fe, dan mengkaji sifat pelepasan Fe(III) dari komposit alginat/zeolit/Fe. Karakterisasi komposit dilakukan dengan mengamati warna komposit secara makroskopik, dan mengamati pola distribusi partikel zeolit dalam komposit dengan menggunakan SEM (Scanning Electron Microscope). Sedangkan untuk mengkaji pelepasan Fe(III) dari sistem komposit dilakukan dengan merendam komposit dalam larutan asam sitrat 0,33M selama sembilan jam. Komponen Fe(III) yang terlarut dalam sistem asam dianalisis dengan menggunakan spektrofotometer UV-Vis. Hasil pengamatan menunjukkan bahwa komposit alginat/zeolit/Fe memilikiwarnawarna yang signifikan bergantung pada perbandingan komponen alginat dan zeolitnya. Analisis SEM menghasilkan informasi bahwa zeolit terdistribusi secara merata pada fasa alginat-Fe.Profil pelepasan Fe(III) dari komposit alginat/zeolit/Fe dengan variasi berat Eksakta: Jurnal Imu-Ilmu MIPA p.
doi:10.20885/eksakta.vol16.iss2.art3 fatcat:bjckq2yc7bghndjcrhgpkrxrpa