This paper describes the effect of cooling rate on the size of the grains, SDAS and thermal characteristic results of the AC AlSi 7 Cu 2 cast alloy. The solidification process was studied using the cooling curve and crystallization curve at solidification rate ranging from 0,16 up to 0,71 C•s-1. It was determined that higher solidification rate increases the aluminum dendrite nucleation temperature and solid fraction at the dendrite coherency point, which implies that mass feeding is extended.

more »

... In addition, it was observed that the non-equilibrium solidus temperature and the size of the grains, SDAS constituent decreases when the solidification rate increases. Описывается влияние скорости охлаждения на величину зерна, расстояние между осями вторичных дендритов и вытекающей термической характеристики литейного сплава AC AlSi 7 Cu 2. Процесс кристаллизации был изучен с использованием кривой охлаждения и кривой кристаллизации при скорости кристаллизации в пределах от 0,16 до 0,71 C•c-1. Было определено, что более высокая скорость кристаллизации увеличивает температуру за-рождения кристаллов дендритов алюминия и твердую фазу в точке когерентности дендри-тов, что подразумевает увеличение подаваемой массы. Наблюдалось, что неравновесная температура перехода в твердое состояние и размер зерен, расстояние между осями вторич-ных дендритов уменьшаются при увеличении скорости кристаллизации.