Isochronous Relaxation Curves for Type 304 Stainless Steel After Monotonic and Cyclic Strain
1979
Journal of Testing and Evaluation
Preserved Fulltext
Relaxation tests to 100 hr were performed on type 304 stainless steel in the temperature range 480 to 650°C and were used to develop isochronous relaxation curves. Behavior after inonotonic and cyclic strain was compared. Relaxation differed only slightly as a consequence of the type of previous strain, provided that plastic flow preceded the relaxation period. We observed that the short-time relaxation behavior did not manifest strong heat-to-heat variation in creep strength. Research