THERMAL PROPERTIES OF CARBOXYMETHYL CELLULOSE ACETATE BUTYRATE

MOHAMED EL-SAKHAWY, Cellulose and Paper Department, National Research Centre, 33, El Bohouth Str., P.O. 12622, Dokki Giza, Egypt, HEBAT-ALLAH S. TOHAMY, AHMED SALAMA, SAMIR KAMEL, Cellulose and Paper Department, National Research Centre, 33, El Bohouth Str., P.O. 12622, Dokki Giza, Egypt, Cellulose and Paper Department, National Research Centre, 33, El Bohouth Str., P.O. 12622, Dokki Giza, Egypt, Cellulose and Paper Department, National Research Centre, 33, El Bohouth Str., P.O. 12622, Dokki Giza, Egypt
2019 Cellulose Chemistry and Technology  

Preserved Fulltext

fulltext thumbnail
Web Archive Capture PDF (662.7 kB)
https://web.archive.org/web/20200211084431/http://www.cellulosechemtechnol.ro/pdf/CCT7-8(2019)/p.667-675.pdf

A copy of this work was available on the public web and has been preserved in the Wayback Machine. The capture dates from 2020; you can also visit the original URL. The file type is application/pdf.

From α-cellulose extracted from sugar cane bagasse, carboxymethyl cellulose (CMC), carboxymethyl cellulose acetate (CMCA) and carboxymethyl cellulose acetate butyrate (CMCAB) have been prepared, characterized and evaluated by TGA and DSC. TGA decomposition curves of CMCAB showed three decomposition stages, while cellulose, CMC and CMCA revealed two decomposition stages. The TGA of cellulose and CMC showed residual weight of 19.6 and 34.2%, respectively, at 600 °C, which indicates the presence
more » ... a fraction of non-volatile components. Meanwhile, the residual weight of CMCA and CMCAB was very low, which indicates their high purity. The activation energy and thermal stability of CMCAB were higher than those of the other derivatives due to the decomposition of the amorphous part during the modification. The DSC curves showed that CMCAB is a glassy thermoplastic material with glass transition temperature of 138.35 °C, whereas endothermic melting was found at 200 °C.
doi:10.35812/cellulosechemtechnol.2019.53.65 fatcat:i22qujbsdzcvlasl4otrw5dgf4
Open Access
Citation

MOHAMED EL-SAKHAWY, Cellulose and Paper Department, National Research Centre, 33, El Bohouth Str., P.O. 12622, Dokki Giza, Egypt, HEBAT-ALLAH S. TOHAMY, AHMED SALAMA, SAMIR KAMEL, Cellulose and Paper Department, National Research Centre, 33, El Bohouth Str., P.O. 12622, Dokki Giza, Egypt, Cellulose and Paper Department, National Research Centre, 33, El Bohouth Str., P.O. 12622, Dokki Giza, Egypt, Cellulose and Paper Department, National Research Centre, 33, El Bohouth Str., P.O. 12622, Dokki Giza, Egypt. "THERMAL PROPERTIES OF CARBOXYMETHYL CELLULOSE ACETATE BUTYRATE." Cellulose Chemistry and Technology 53.7-8 (2019) 667-675