Effect of Forming Temperature on Spring-back in Hot Forming Quenching of AA6061 Sheet
AA6061 판재의 핫 포밍 �칭 공정에서 성형온도가 스프링백에 미치는 영향

I.B. Shim, J.H. Kim, B.M. Kim
2017 Transactions of Materials Processing  
Aluminum alloys are widely used in automotive industry because of their high strength-to-density ratio and excellent corrosion resistance. However, conventional cold stamping of aluminum alloys leads to low formability and excessive spring-back. To overcome these problems, Hot Forming Quenching (HFQ) is applied to manufacture automotive part using aluminum alloy. The purpose of this study is to investigate effect of forming temperature on spring-back in HFQ of T6 heat treated AA6061 sheet. In
more » ... AA6061 sheet. In this study, hat shape forming test was adopted to evaluate spring-back characteristics according to various forming temperatures. In additions, the test was also performed with warm forming conditions in comparison with dimensional accuracy of HFQed part. The experimental results showed that dimensional accuracy of HFQed part was superior to warm formed part and amount of spring-back was decreased as forming temperature rise. 1. 서 론 전세계적으로 차체 경량화를 위해 알루미늄을 이 용한 차체 부품의 제조 및 적용이 확대되고 있다. 알루미늄은 높은 비강성, 우수한 내부식성 등의 이 점을 가지며, 후드와 팬더, 도어 등에 주로 적용되 고 있다[1, 2]. 일반적으로 알루미늄을 이용한 차체 부 품은 냉간 스탬핑 공정으로 제조되고 있으나, 낮은 성형성과 과도한 스프링백 등의 문제가 발생한다[3]. 최근 이러한 문제를 해결하기 위해 알루미늄 판재를 이용한 핫 포밍 퀜칭 공정(hot forming quenching; HFQ) 이 제안되었다[4]. HFQ는 용체화처리 온도로 가열된 소재를 냉각채 널이 설치된 금형을 이용하여 성형 및 퀜칭을 동시 에 진행하는 방법이다. HFQ은 열간 성형이므로 성 형성 향상, 스프링백 저감, 후열처리 공정의 제거 등이 가능한 공정이다. 이에 따라 많은 연구자들에 의해 HFQ에 대한 연구가 활발하게 진행되고 있다. Yuan 등[5]은 2A12의 HFQ에서 금형의 온도가 소 재의 조직 및 물성에 미치는 영향을 조사하였다. 그 결과, 상형은 냉간, 하형은 450℃로 가열한 조건에 서 균일한 석출로 인해 높은 기계적 물성을 갖는다 는 것을 확인하였다. 또한, Ko 등[6]은 에릭슨 테스 트(Erichsen test)와 V-bending 실험을 통해 AA6061의 HFQ과 냉간 성형 공정의 성형성 및 기계적 특성을 평가하였다. Fan 등[7]은 AA6A02의 HFQ에서 냉간 1. 부산대학교 기계공학부 정밀가공시스템 전공
doi:10.5228/kstp.2017.26.2.101 fatcat:lxlfd2an7vamfdwnvgusow2gqe