Copper impregnated aluminum pillared montmorillonites (Cu-iAlpill-MMTs) were prepared by adding Cu2+ solution into dried aluminum polyohydroxy cation intercalated montmorillonite using various Cu2+ concentrations, i.e. 4, 7, 10 and 13 wt% and then calcining at 500°C. The Cu-iAlpill-MMTs possessed slit-liked mesopores with pore diameters of 3.3–3.8 nm and ~6–35 nm as observed from the nitrogen adsorption isotherms. The mesopore quantities of Cu-iAlpill-MMTs gradually decreased with the increasedoi:10.1515/bpasts-2016-0062 fatcat:rli4nhlwfzbbflbdh3fliofpiy