Abstrak ___________________________________________________________________ Penelitian ini dilakukan uji kuat tekan beton, modulus elastisitas, dan serapan air beton. Benda uji kuat tekan dan modulus elastisitas beton berbentuk silinder dengan diameter 150 mm dan tinggi 300 mm. Sedangkan benda uji untuk pengujian serapan air berbentuk kubus dengan panjang sisi 150 mm. Kuat tekan beton diuji pada umur 3, 7, 14, 28, 60, dan 90 hari. Sedangakan pengujian modulus elastisitas dan serapan air beton

more »

... uji pada umur 28, 60, dan 90 hari. Hasil uji kuat tekan pada umur 3, 7, 14, 28, 60, dan 90 hari yaitu 12,. Laju kenaikan kuat tekan beton didapat prosentase pada umur tersebut sebesar 39,68%, 65,01%, 86,36%, 100%, 111,24%, dan 120,12%. Prosentase serapan air pada beton semakin berkurang seiring bertambahnya umur beton yaitu pada umur 28, 60, dan 90 hari sebesar 3,807%, 2,341%, dan 1,852%. Nilai modulus elastisitas beton pada umur 28, 60 dan 90 hari yaitu 20.150 Mpa, 22.736 Mpa, dan 24.886 Mpa. Pada tegangan maksimum, regangan beton diperoleh rata-rata 0,00257. Hasil modulus elastisitas pada penelitian ini didapatkan E = 4210√fc'. Abstract ___________________________________________________________________ Test specimen compressive strength and modulus of elasticity is a cylindrical with a diameter of 150 mm and height 300 mm. While the water absorption test specimen used cube with side length of 150 mm. The compressive strength of concrete tested at the age of 3, 7, 14, 28, 60, and 90 days. While testing the modulus of elasticity and water absorption of concrete tested at 28, 60, and 90 days. The test results of compressive strength tested at age of 3, 7, 14, 28, 60, and 90 days are 12,. The rate of compressive strength concreate get percentage at ages are 39,68%, 65,01%, 86,36%, 100%, 111,24%, dan 120,12%. The water absorption test on the concrete decreased percentage at 28, 60, and 90 days are 3,807%, 2,341%, dan 1,852%. The modulus of elasticity at age 28, 60, and 90 days are 20.150 Mpa, 22.736 Mpa, dan 24.886 Mpa. At maximum voltage, the concrete strain obtained an average of 0.00257. The results of the study indicated the modulus of elasticity E = 4210√fc'.