The Effect of pH on Synthesis of Hydroxyapatite from Geloina Coaxans Shell

Pepi Helza Yanti, Nia Nia
2017 IPTEK Journal of Proceedings Series  
The effect of pH on synthesis of hydroxyapatite from Geloina coaxans shell has been done by precipitation method. Geloina coaxans shells and several phosphate sources (NH4)2 HPO4 and H3PO4 were used as precursors on synthesis of HAp. Synthesis of HAp was done with molar ratio of precursors 1,67 and pH of solution were varied at 10, 12, 13, and 14. The result proved that nano-HAp can be obtained successfully and shown that pH value was a significant parameter variable on synthesis HAp that can
more » ... fluence crystalinity and purity of HAp. Using Schererr equation, particle size of HAp powder of (NH4)2HPO4 was 26,69 while H3PO4 was 40 nm respectively. ABSTRAK Pengaruh pH pada sintesis hidroksiapatit mengggunakan cangkang lokan (Geloina coaxans) telah dilakukan menggunakan metode pengendapan. Cangkang lokan (Geloina coaxans) dan beberapa sumber posfat seperti (NH4)2 HPO4 dan H3PO4 telah digunakan sebagai prekursor pada sintesis senyawa hidroksiapatit. Sintesis senyawa hidroksiapatit ini dilakukan dengan perbandingan molar prekursor 1,67 dan pH larutan divariasikan pada 10, 12, 13, dan 14. Hasil yang diperoleh menunjukkan bahwa nano-hidroksiapatit dapat diperoleh melalui variasi pH, dan membuktikan bahwa pH merupakan suatu parameter penting dalam sintesis hidroksiapatit yang dapat mempengaruhi kristalinitas dan kemurnian dari hidroksiapatit yang dihasilkan. Dengan menggunakan persamaan Schererr, ukuran partikel hidroksiapatit yang yang dihasilkan (NH4)2HPO4 adalah 26,69 sedangkan H3PO4 adalah 40 nm Kata kunci: Geloina coaxans, HAp, (NH4)2HPO4 and H3PO4
doi:10.12962/j23546026.y2017i4.3073 fatcat:3uyffpexkzebnl445qzjwwdomq