In this paper, nickel-plated carbon fiber was fabricated by a dry process method to improve electromagnetic wave shielding performance. In general, carbon fiber is wrapped in a polymer type in manufacturing and is used after removing the sizing in the pretreatment step for dry coating. The existing sizing removal method was used by removing only with a solution or only with compressed air. In this paper, the method of solution and compressed air (hybrid) was added. The state in which the sizing

more »

... was removed was determined only by the know-how of the experienced person, and in this paper, it is proposed to represent the numerical value by applying the image processing surface analysis technique. As a result, it was possible to numerically indicate that the hybrid method was excellent among the sizing removal methods and it was possible to manufacture the nickel-plated carbon fibers (30 μm, 40 μm, and 100 μm) by a roll-to-roll sputtering method on the sizing-removed spreading carbon fiber roll. The electromagnetic wave shielding performance of 100 nickel-coated carbon fiber measured by the Korea Testing Laboratory showed the highest electromagnetic wave shielding performance from 66.7 (dB) to 73.2 (dB). This is similar to the electromagnetic wave shielding rate of copper, so it can be used as a cable for EV/HEV vehicles, and it is expected to have a great effect of improving the bending characteristics and disconnection phenomenon and improving the lifespan compared to the existing copper wire.