SINTESIS NANO KRISTALIN KOMPOSIT ALUMINA-ZIRKONIA DENGAN TEMPLATE PULP ORYZA SATIVA MELALUI METODE KALSINASI PREKURSOR SYNTHESIS OF NANO-ALU MINA COMPOSITE CRYSTALLINE ZIRKONIA ORYZA SATIVA PULP BY TEMPLATE METHOD PRECURSOR CALCINATION

Frank, Bambang Purwasasmita, Suhanda, Rifki Septawendar, Leanddas Nurdiwijayanto, Balai Keramik, Kementrian Perindustrian Indonesia
2011 Jurnal Riset Industri   unpublished
ABSTRAK Nano kristalin komposit alumina-zirkonia disintesis melalui metode kalsinasi prekursor dengan pulp oryza sativa sebagai template serta Al(NO3)3.9H2O dan ZrCl4 sebagai prekursor dengan komposisi molar 80:20. Pencampuran prekursor, pelarut, dan pulp menggunakan ultra turrax T25 pada RPM 15000 selama 3 menit sebanyak 3 kali. Kalsinasi yang ditujukan untuk memperbaiki morfologi dan pembentukan fasa dilakukan pada temperatur 900, 1000, 1100, 1200, dan 1250°C. Untuk mengetahui sifat-sifat
more » ... material komposit yang terbentuk, dilakukan karakterisasi X-Ray Diffraction (XRD) dan Scanning Electron Microscope (SEM). Dari hasil XRD, dapat diidentifikasi fasa dari komposit yang muncul, yaitu tetragonal-zirkonia, monoklinik-zirkonia, dan δ-alumina. Fasa tunggal tetragonal-zirkonia muncul pada sampel yang dikalsinasi pada temperatur 900-1100°C, sementara sampel yang dikalsinasi pada temperatur yang lebih tinggi menghasilkan fasa campuran antara tetragonal-zirkonia dan monoklinik-zirkonia. Dari hasil SEM, terlihat bahwa morfologi partikel memiliki bentuk menyerupai bentuk dari pulp, yang mana bentuk ini merupakan akibat dari pencampuran dengan kecepatan tinggi. Kata kunci: Komposit, ABSTRACT Nanocrystalline composite alumina-zirconia has been successfully synthesized by precursor calcining process with oryza sativa pulp as template. The synthesis of alumina-zirconia composite was done using Al(NO3)3.9H2O and ZrCl4 as precursors with molar ratio of 80:20. The mixing of precursors, solvent, and pulp was carried out by means of ultra turrax T25 homogenizer at 15000 rpm for 3 times with each for 3 minutes. The calcination process for the formation of the phase of alumina-zirconia composite was performed at 900, 1000, 1100, 1200, and 1250°C. To indentify the properties of alumina-zirconia composite, the X-Ray Diffraction (XRD) and Scanning Electron Microscope (SEM) need to be employed. Based on XRD analysis result, it can be seen that the phase of alumina-zirconia composite are tetragonal-zirconia, monoclinic-zirconia, and δ-alumina. The single phase of tetragonal-zirconia appears for samples annealed at 900-1100°C; while for sampels annealed at 1200°C and 1250°C, it appears to have multiphase of tetragonal-zirconia and monoclinic-zirconia. The transformation of singlephase of tetragonal-zirconia to multiphase of tetragonal-zirconia and monoclinic-zirconia is believed to be due to the increase of crystallite size as the calcination temperature increased, thus causes the subsequent growth of the crystalls. According to SEM micrograph, it can be seen that the morphology of particles has a shape resemble to the morphology of pulp, which is the effect of mixing at high RPM.
fatcat:3af3nvi3sfc2javxgo4lj4madu