Hot Rolling of Magnesium Single Crystals
2021
Metals
To analyze the effect of the initial orientation in the activity of twinning and texture development, magnesium single crystals were rolled at 400 °C (nominal furnace temperature) in two specific orientations. In both orientations, the rolling direction of the sheet (RD) was parallel to the c-axis. For orientation 1, the 112¯0 direction was parallel to the normal direction (ND), and for orientation 2, it was parallel to the 101¯0 direction. The samples were rolled at 30%, 50% and 80% of