Hydration and properties of ternary cement with calcareous filler and slag

E. F. Irassar, V. L. Bonavetti, G. Menéndez, M. F. Carrasco
2015 Revista ALCONPAT  
<p><strong>ABSTRACT</strong></p><p>The calcareous filler produces an increase in early hydration due to the physical effects (filler and heterogeneous nucleation). The dilution effect counteracts this benefit and limits its content. Slag reacts slowly, causes the refinement of grains and pores, and improves the mechanical and durable properties. This paper is a study on the hydration of cements with filler (0 to 20%) and slag (0 to 35%), utilizing the Powers model for slag expanded by Chen
more » ... panded by Chen &amp; Brouwers. The mechanical resistance of the concrete (a/mc = 0.50) and the segmentation of the pores in relation to the capillary absorption rate are analyzed from the hydration results. The results show a limit on the filler content to obtain an adequate response for the mechanical and durable resistances at a greater age, and a limit on the slag content to obtain appropriate values at an early age.</p><p class="Ttuloresumen"><strong>Keywords:</strong> Calcareous filler; Slag; Resistance; Capillary absorption; Hydration.</p><p class="Ttuloresumen"><span style="text-decoration: underline;"><strong><br /></strong></span></p><p class="Ttuloresumen"><span style="text-decoration: underline;"><strong>Hidratación y propiedades de cemento ternarios con filler calcáreo y escoria</strong></span></p><p class="Ttuloresumen"><strong>RESUMEN</strong></p><p>El filler calcáreo produce un incremento de la hidratación temprana debido al efecto físico (relleno y nucleación heterogénea). El efecto de dilución contrarresta este beneficio y limita su contenido. La escoria reacciona lentamente, provoca el refinamiento de granos y poros, y mejora las propiedades mecánicas y durables. En este trabajo se estudia la hidratación de cementos con filler (0 a 20 %) y Escoria (0 a 35%), empleando el modelo de Powers ampliado por Chen &amp; Browers para escoria. A partir de los resultados de la hidratación, se analizan la resistencia mecánica del hormigón (a/mc = 0.50), y el proceso de segmentación de poros en relación con la tasa de absorción capilar. Los resultados muestran una limitación del contenido de filler para obtener una respuesta adecuada de la resistencia mecánica y durable a largas edades, y del contenido de escoria para obtener valores apropiados a temprana edad.<strong></strong></p><p class="Normalresumen"><strong>Palabras clave: </strong>Filler calcáreo; escoria; resistencia; absorción capilar; hidratación</p><p><strong><span style="text-decoration: underline;"><br /></span></strong></p><p><strong><span style="text-decoration: underline;">Hidratação e propriedades de cimentos compostos (com três adições) com fíler calcário e escória</span></strong></p><p class="Ttuloresumen"><strong>RESUMO</strong></p><p>Filler calcário produz uma aceleração da hidratação nas primeiras idades devido ao efeito físico (compactação e nucleação heterogênea). O efeito de diluição neutraliza os benefícios e limita o seu conteúdo. A escória reage lentamente, fazendo com que o refinamento dos grãos e poros, e melhora as propriedades mecânicas e duráveis. Neste trabalho a hidratação do cimento com filler (0-20%) e escória (0-35%) é estudada usando o modelo de Powers ampliado por Chen Browers para escória de alto forno. A partir dos resultados de hidratação, é analisada a resistência do concreto (com a /c = 0,50), e o processo de segmentação de poros é analisado com relação a taxa de absorção capilar. Os resultados mostram que o teor de filler deve ser limitado para obter uma resposta de resistência mecânica e de durabilidade. Também o conteúdo de escória deve ser limitado para obter propriedades adequadas nas primeiras idades.<strong></strong></p><p class="Normalresumen"><strong>Palavras chave: </strong>Filler calcário; escória; resistencia; absorção capilar; hidratação.</p>
doi:10.21041/ra.v5i2.79 fatcat:nbe7rak5pbffzmtaxvtnvxhjwe