Impact of firing temperature on insulating properties of Low Temperature Co-fired Ceramics

Arkadiusz P. Dabrowski
2020 Materials Science-Poland  
AbstractIn this paper, results of investigation on the impact of firing temperature on insulating properties of Low Temperature Cofired Ceramics are presented. Dissipation factor, volume resistivity and breakdown electric field intensity were determined for firing peak temperature in the range from 800 °C to 900 °C. The tests were performed for two commercial LTCC materials: 951 Green Tape (DuPont, USA) and SK47 (Keko, Slovenia). The results showed that the firing temperature had a significant
more » ... had a significant effect on the dielectric loss factor, volume resistivity and lifetime at applied high voltage. No clear tendency was observed for dielectric strength in the analyzed firing temperature range.
doi:10.2478/msp-2020-0012 fatcat:ijgqbpvsjzffvkm5y7mpassqci