Influence of aluminum substitution on the fi eld of effective magnetic anisotropy and the degree of magnetic texture of anisotropic polycrystalline hexagonal ferrites of barium and strontium for substrates of microstrip devices of microwave electronics

S. V. Shcherbakov, A. G. Nalogin, V. G. Kostishin, A. A. Alekseev, E. A. Belokon, I. M. Isaev
2019 Izvestiya Vysshikh Uchebnykh Zavedenii Materialy Elektronnoi Tekhniki = Materials of Electronics Engineering  

Preserved Fulltext

fulltext thumbnail
Web Archive Capture PDF (439.6 kB)
https://web.archive.org/web/20200213200301/https://met.misis.ru/jour/article/download/332/262

A copy of this work was available on the public web and has been preserved in the Wayback Machine. The capture dates from 2020; you can also visit the original URL. The file type is application/pdf.

Abstract. In this paper, the effect of Al3+ ions substitutions on the value of the effective magnetic anisotropy field НАeff and the degree of magnetic texture f of the anisotropic polycrystalline hexagonal barium and strontium ferrites were studied. The samples were obtained by the ceramic technology method and the texture was formed by pressing in a magnetic field. The sample preparation technology presented in detail. The batches of barium hexaferrites were synthesized with the concentration
more » ... of Al3+ ions: 0.9; 1.4; 2.5 and 2.6 formula units while strontium hexaferrites had Al3+ concentration of 0.1 formula units. It has been shown that by this technology barium and strontium hexaferrites with high value of (in range of 19—35 kOe) and with f = 80—83% could be obtained. The achieved values of НАeff and f could be sufficient for the production of substrates for microstrip microwave devices in millimeter−wave region.For the first time a raise in the degree of magnetic texture of polycrystalline barium hexaferrites with an increase of concentration of Al3+ ions were detected; a slight (5.5—5.8%) magnetic texture of isotropic strontium hexaferrites was also detected. The achieved results discussed in detail. For studied hexaferrites the mechanism of magnetic texture formation during the process of synthesis is proposed.
doi:10.17073/1609-3577-2018-3-166-174 fatcat:e5qzilrfovb3bdsvzgcpjubaem
Open Access
Citation

S. V. Shcherbakov, A. G. Nalogin, V. G. Kostishin, A. A. Alekseev, E. A. Belokon, I. M. Isaev. "Influence of aluminum substitution on the fi eld of effective magnetic anisotropy and the degree of magnetic texture of anisotropic polycrystalline hexagonal ferrites of barium and strontium for substrates of microstrip devices of microwave electronics." Izvestiya Vysshikh Uchebnykh Zavedenii Materialy Elektronnoi Tekhniki = Materials of Electronics Engineering 21.3 (2019) 166-174