The study on the characteristics of nitrous oxide catalytic decomposition was carried out to utilize the nitrous oxide as a propellant. The Pt, Ir and Ru were synthesized to select a high performance catalyst for the nitrous oxide decomposition reaction. The respective catalyst precursors were loaded in the Al2O3 support using an wet impregnation method. The N2O conversion as a variation of space velocity and reaction temperature was measured using a tubular reactor. The catalyst loss was

more »

... ed to evaluate the durability of catalysts after the reaction at 800 o C for 2 hours. The N2O conversion was increased at the decrease of space velocity and at the increase of temperature. The Ru/Al2O3 catalyst had the highest N2O conversion at low temperature and the best durability. 초 록 추진제로써 아산화질소를 활용하기 위해 아산화질소의 촉매 분해 특성에 대한 연구를 수행하였다. 아산화질소 분해 반응을 위한 고성능 촉매를 선정하기 위해 Pt, Ir, Ru 촉매 를 합성하였다. 촉매 합성을 위해 각각의 촉매 전구체를 함침법을 이용하여 Al2O3 지지체 에 담지하였다. 제조된 촉매는 관형 반응기를 사용하여 공간속도와 반응온도에 따른 N2O 전환율을 가스 분석을 통해 측정하였다. 또한 촉매 내구성을 판단하기 위해 800 o C에서 2 시간 동안 반응한 후 촉매 유실량을 측정하였다. N2O 전환율은 공간속도가 낮을수록 반 응온도가 높을수록 높았고, Ru/Al2O3 촉매가 낮은 온도에서 가장 높은 N2O 전환율을 보였고 내구성도 가장 우수하였다.