Pengaruh Lama Miling Terhadap Sifat Absorpsi Material Penyimpan Hidrogen MgH2 yang Dikatalisasi Dengan Fe (The Role of Milling Time on the Absorption Behaviour of MgH2 Catalyzed by Fe)

Mustanir Mustanir, Zulkarnain Jalil
2009 Bulletin of Chemical Reaction Engineering & Catalysis  
PENDAHULUAN Penelitian sistem penyimpanan hidrogen kenderaan fuel cell saat ini sangat intensif dilakukan. Dikenal ada tiga metode penyimpanan, yakni dalam bentuk gas, cair dan padat. Dua metode pertama yaitu dalam bentuk gas (pada tekanan tinggi 700 bar) dan cair (suhu harus tetap stabil pada - Abstract Hidrida logam berbasis MgH2 dengan sisipan 1 wt% katalis Fe telah berhasil disintesis dengan teknik ball milling. Hasil proses miling selama 80 jam menunjukkan bahwa ukuran butir material telah
more » ... utir material telah membentuk struktur nanokristal. Hal ini ditunjukkan oleh profil difraksi sinar-X dimana terjadi pelebaran puncakpuncak difraksinya dengan meningkatnya waktu miling. Hasil uji absorpsi secara gravimetrik diketahui bahwa MgH2 berkatalis 1 wt% Fe mampu menyerap hydrogen sebesar 5,5 wt% dalam waktu ~20 menit pada temperatur 300 o C. Hasil ini sekaligus memperlihatkan bahwa sejumlah kecil katalis Fe bekerja secara baik dalam memperbaiki sifat absorpsi material penyimpan hydrogen berbasis Mg. © 2009 BCREC. All rights reserved (Metal hydrides are of great interest as hydrogen storage media especially for automotive application. Hydrides of magnesium and magnesium alloys are particularly attractive as they combine potentially high hydrogen storage capacities, 7.6 wt%. But, unfortunately, the sorption properties are poor. For example, conventional hydrogenation of magnesium requires prolonged treatment at temperatures of 300 o C and above. Here, we report the absorption properties of MgH 2 catalyzed with a small amount of Fe element (1wt%) under argon atmosphere prepared by ball milling in 80 hours. As the results, it showed the influence of milling time on the absortion kinetics of material which could absorp hydrogen in amount 5.5 within 20 minutes at 300 o C. It is obvious that longer milling time and small amount of catalyst could improve the sorption properties of Mg-based hydrides). 253 0 C) dari sisi keamanan belum memadai. Sistem penyimpan mutakhir yang saat ini aktif diteliti adalah dengan menggunakan teknik penyimpan padat (solid hydrogen storage). Dalam sistem padat ini atom-atom H berada pada kisikisi material utamanya, dimana hidrogen "disisipkan" dalam material tertentu. Kini arah penelitian terfokus pada upaya untuk mendapat-
doi:10.9767/bcrec.4.2.32.69-72 fatcat:vctt3xvvmrft3myvekypz35jzq