Tribological Properties of PPS/PA46 Polymer Blends

Ferhat Yıldırım, Machinery and Metal Technologies Department, Biga Vocational School, Çanakkale Onsekiz Mart University, Mustafa Aydın, Hakan Yetgin, Mechanical Engineering Department, Hasan Ferdi Turgutlu Technologie Faculty, Manisa Celal Bayar University, Mechanical Engineering Department, Simav Technologie Faculty, Kütahya Dumlupınar University
2020 Research on Engineering Structures and Materials  
In this study, the tribological performance of originally 40 wt.% fiber glass reinforced polyphenylene sulfide (PPS-G), polyamide 46 (PA46) and their blends were studied at dry sliding conditions. The materials were mixed and extruded on the twin screw extruder. The blends were dried and tribological test specimens were manufactured by using the injection machine. Wear tests were performed with the configuration of a polymer pin on a rotating X40CrMoV5-1 steel disc. Test conditions were
more » ... itions were atmospheric conditions having 60, 90, 120 N loads and 0.5, 1.0, 1.5 m/s sliding speeds. The obtained results proved that the coefficient of friction for PPS-G, PA46 and their blends is decrease while the applied load and sliding speed values are increase. On the other hand, the specific wear rate is in increase while the applied load and sliding speed values are in increase.
doi:10.17515/resm2019.144ma0607 fatcat:oh7jur7fc5alnhyfbgsds3juym