Pengaruh Variasi Temperatur Hardening dan Tempering Paduan AlMgSi-Fe12% Hasil Pengecoran terhadap Kekerasan

Sumpena Sumpena, Wardoyo Wardoyo
2018 Jurnal Engine: Energi, Manufaktur, dan Material  
<p>The purpose of this research is to know the effect of Heat Treatment Hardening-Tempering Alloy AlMgSi–Fe12% foundry result to hardness and toughness. The test was carried out on raw material and material test specimen after obtaining Hardening heat treatment at 600℃ and quenching with SAE 20 oil medium. While Tempering variation at temperature 200℃, temperature 250℃ and temperature 300℃ with detention time for 15 min at each temperature, each heat treatment. Hardness testing method is done
more » ... standard micro Vickers test method with 100 gf loading. The result of raw material testing for hardness value is 60,92 VHN. Test results after heat treatment process at temperature 200℃ cause hardness value increased by 63,50 VHN. At temperature 250℃ cause hardness value decreased to 59,94 VHN. At temperature 300℃ cause hardness value increase to 76,98 VHN </p>
doi:10.30588/jeemm.v2i1.357 fatcat:aag4ec6f5bdpbnkruuptat6qhy