This research was conducted at the Laboratory of Material Testing and Civil Engineering Construction, Halu Oleo University. This research guideline refers to SNI (Indonesian National Standard). Quality of concrete f'cr 20 Mpa. With the percentage addition of glass bottle waste fragments of 0%, 10%, 15%, and 20% of the weight of fine aggregate. The concrete compressive strength test was carried out at the age of 7 days, 14 days, and 28 days . The results of the average compressive strength

more »

... ed starting at the immersion age of 28 days with a percentage of 0% without glass, the quality of the concrete obtained is 17.15 MPa. at a percentage of 10% by using additional waste glass bottles with the quality of the concrete obtained is 18.97 MPa. has increased for 28 days of age from a percentage of 0% to 10%, namely 10.61%. Furthermore, at a percentage of 15% by using additional waste glass bottles with the quality of the concrete obtained is 18.45 MPa. has increased for the age of 28 days the percentage of 0% to 15% is 7.58%. Furthermore, the percentage of 20% by using additional glass bottle waste with the quality of the concrete obtained is 17.93 MPa, an increase for 28 days, the percentage is 0% to 20%, namely 4.55%Penelitian ini dilaksanakan di Laboratorium Pengujian Bahan dan Konstruksi Teknik Sipil Universitas Halu Oleo. Pedoman penelitian ini mengacu pada SNI (Standar Nasional Indonesia). Mutu beton f'cr 20 Mpa. Dengan persentasi penambahan pecahan limbah botol kaca sebesar 0%, 10%, 15%, dan 20% dari berat agregat halus. Pengujian kuat tekan beton dilakukan pada umur 7 hari, 14 hari, dan 28 hari.Penelitian ini dilaksanakan di Laboratorium Pengujian Bahan dan Konstruksi Teknik Sipil Universitas Halu Oleo. Pedoman penelitian ini mengacu pada SNI (Standar Nasional Indonesia). Mutu beton f'cr 20 Mpa. Dengan persentasi penambahan pecahan limbah botol kaca sebesar 0%, 10%, 15%, dan 20% dari berat agregat halus. Pengujian kuat tekan beton dilakukan pada umur 7 hari, 14 hari, dan 28 hari.Hasil kuat tekan rata-rata yang di dapatkan mulai pada umur perendaman 28 hari dengan presentase 0% tanpa kaca mutu beton yang di dapatkan yaitu 17.15 Mpa. pada presentase 10% dengan menggunakan tambahan limbah botol kaca dengan mutu beton yang di dapatkan yaitu 18,97 Mpa. mengalami peningkatan untuk umur 28 hari dari presentase 0% ke 10% yaitu 10,61 %. Selanjutnya pada presentase 15% dengan menggunakan tambahan limbah botol kaca dengan mutu beton yang di dapatkan yaitu 18,45 Mpa. mengalami peningkatan untuk umur 28 hari presentase 0% ke 15% yaitu 7,58%. Selanjutnya pada presentase 20% dengan menggunakan tambahan limbah botol kaca dengan mutu beton yang di dapatkan yaitu 17,93 Mpa, mengalami peningkatan untuk umur 28 hari presentase 0% ke 20% yaitu 4,55%