Nanocrystalline Cadmium sulfide (CdS) thin film synthesized at different dip times by chemical bath deposition technique
English

A Ezekoye B, O IGHODALO K, A Ezekoye V, M Emeakaroha T, I Ezema J, O Offor P
2015 International Journal of Physical Sciences  
Nanocrystalline Cadmium sulfide (CdS) thin films were prepared by chemical bath deposition technique on a glass substrates at a temperature of 80°C and at different deposition times with composition of cadmium chloride (CdCl 2 ), thiourea (CS (NH 2 ) 2 ), ammonia solution (NH 4 OH) and triethanolamine (TEA) solution. The characterization of thin films was carried out for the structural, morphological and optical properties using X-ray diffraction (XRD), Scanning electron microscope (SEM) and
more » ... VIS spectrophotometer. XRD studies show that the preferential orientation (002), analysis shows that the prepared samples have hexagonal crystal structure. Scanning electron microscopy (SEM) reveals small nanosized grains tied up in a fibrous-like porous structure uniformly distributed over the surface of the substrate for the CdS films. A UV-VIS optical spectroscopy study was carried out to determine the band gap of the nanocrystalline CdS thin films. The average band gap was found to be 2.25 eV, which is lower than the bulk value (2.4 eV). The increase in absorption coefficient with photon energy makes the deposited CdS thin film a suitable candidate for the fabrication of solar cells.
doi:10.5897/ijps2015.4360 fatcat:i5c4fslujzaqjffvabuwnlbkku