Aluminum alloys with 0% (wt.%), 0.15% and 0.30% Er were subjected to micro-arc oxidation under the same parameters. The surface morphology and the phases of the oxide coating were analyzed using SEM and XRD. The microhardness, thickness and corrosion resistance of the oxide coating were also studied. The results show that the micro-arc oxidation coating on a 7075 aluminum alloy with different Er contents is composed of the gamma-Al2O3 phase. With increasing Er content, the peak of the

more »

... 3 phase becomes stronger. Er enters the oxide coating in the form of Al17Er2, which is an unbalanced phase under micro-arc oxidation. With increasing Er content, the surface deposits become finer and more uniform, the microhole diameter decreases, and the flatness increases. As the Er content increases from 0% to 0.30%, the micro-hardness and thickness of the oxide coating also increase, and then the corrosion resistance increases significantly. Consequently, the self-corrosion current density decreases from 4280.0 nA/cm 2 to 2.405 nA/cm 2 .