EFFECT OF COOLING RATE ON THE SOLIDIFICATION BEHAVIOR OF AC AlSi 7 Cu 2 ALLOY release_uqway6czijgn3pibrydutzvra4

Abstract

This paper describes the effect of cooling rate on the size of the grains, SDAS and thermal characteristic results of the AC AlSi 7 Cu 2 cast alloy. The solidification process was studied using the cooling curve and crystallization curve at solidification rate ranging from 0,16 up to 0,71 C•s-1. It was determined that higher solidification rate increases the aluminum dendrite nucleation temperature and solid fraction at the dendrite coherency point, which implies that mass feeding is extended. In addition, it was observed that the non-equilibrium solidus temperature and the size of the grains, SDAS constituent decreases when the solidification rate increases. Описывается влияние скорости охлаждения на величину зерна, расстояние между осями вторичных дендритов и вытекающей термической характеристики литейного сплава AC AlSi 7 Cu 2. Процесс кристаллизации был изучен с использованием кривой охлаждения и кривой кристаллизации при скорости кристаллизации в пределах от 0,16 до 0,71 C•c-1. Было определено, что более высокая скорость кристаллизации увеличивает температуру за-рождения кристаллов дендритов алюминия и твердую фазу в точке когерентности дендри-тов, что подразумевает увеличение подаваемой массы. Наблюдалось, что неравновесная температура перехода в твердое состояние и размер зерен, расстояние между осями вторич-ных дендритов уменьшаются при увеличении скорости кристаллизации.
In text/plain format

Archived Files and Locations